ABS
P430 ABSplus Material Properties
MECHANICAL PROPERTIES 1
| Test Method | Imperial | Metric | |
|---|---|---|---|
| Tensile Strength, Type 1, 2 in/min (51 mm/min) 0.125 | ASTM D638 | 5,300 psi | 37 MPa |
| Tensile Modulus, Type 1, 2 in/min (51 mm/min) 0.125 | ASTM D638 | 330,000 psi | 2,320 MPa |
| Tensile Elongation, Type 1, 2 in/min (51 mm/min) 0.125 | ASTM D638 | 3% | 3% |
| Flexural Delamination | ASTM D790 | 4,500 psi | 31 MPa |
| Flexural Strength | ASTM D790 | 7,600 psi | 53 MPa |
| Flexural Modulus | ASTM D790 | 320,000 psi | 2250 MPa |
| IZOD Impact, notched, (Method A, 73° (23° C)) | ASTM D256 | 2.0 ft-lb/in | 106 J/m |
THERMAL PROPERTIES 3
| Test Method | Imperial | Metric | |
|---|---|---|---|
| Heat Deflection (HDT) @ 66 psi (0.5 MPa) | ASTM D648 | 204°F | 96°C |
| Heat Deflection (HDT) @ 264 psi (1.8 MPa) | ASTM D648 | 180°F | 82°C |
| Glass Transition (TG) | DMA (SSYS) | 226° F | 108°C |
| Melt Point | (NA)2 | (NA)2 |
OTHER 3
| Test Method | Value | |
|---|---|---|
| Specific Gravity | ASTM D792 | 1.04 |
| Vertical Burning Test | UL94 | HB |
| Coefficient of Thermal Expansion | ASTM E831 | 4.90E-05 in/in/F |
| Dielectric Strength (kV / mm) | IEC 60112 | 28.0 |
1 Build orientation is on side edge except for flexural delamination which is upright.
2 Not applicable (NA) due to amorphous nature. Material does not display a melting point.
3 Literature value unless otherwise noted.